AgGaS2 crystals


  • Halbeegyada Lattice:a = 5.757, c = 10.311 Å
  • Meesha dhalaalaysa:997 °C
  • Cufnaanta:4.702 g/cm3
  • Mohs Hardness:3-3.5
  • Iskuxidhka Nuugista:0.6 cm-1 @ 10.6 µm
  • Joogtada Dielectric Qaraabo @ 25:ε11s=10ε11t=14
  • Faahfaahinta Alaabta

    Qiyaasta Farsamada

    Warbixinta Imtixaanka

    Liiska saamiyada

    AGS waa hufan laga bilaabo 0.50 ilaa 13.2 µm.In kasta oo isku-dheellitirkeeda indho-indheynta aan tooska ahayn uu yahay kan ugu hooseeya ee ka mid ah kiristaalo infrared-ka ee la sheegay, daah-furnaanta hirarka gaaban ee dhererka sare ee 550 nm ayaa lagu sameeyay isticmaalka OPO-yada ay ku shubto Nd:YAG laser;Tijaabooyin isku dhafan oo kala duwan oo badan oo kala duwan oo isku dhafan oo leh diode, Ti: Sapphire, Nd: YAG iyo IR dheeha leysarka oo daboolaya kala duwanaanta 3-12 µm;Nidaamyada cabbiraadda tooska ah ee infrared, iyo SHG ee CO2 laser.Taarikada khafiifka ah ee AgGaS2 (AGS) waxay caan ku yihiin jiilka garaaca wadnaha ee ultrashort ee dhexda IR kala duwanaanshaha jiilka soo noqnoqda ee isticmaalaya garaacyada hirarka hirarka NIR.

    Codsiyada:
    • Jiilka labaad ee harmonics ee CO iyo CO2 - lasers
    • oscilator parametric indhaha
    Dhaliyaha soo noqnoqda ee kala duwan ilaa gobolada dhexe ee infrared ilaa 12μm.
    • Isku darka inta jeer ee gobolka IR ee dhexe laga bilaabo 4.0 ilaa 18.3 µm
    Laysarka gobolka adag ee la dami karo (OPO oo ay bamgarayso Nd:YAG iyo lasers kale oo ka shaqeeya 1200 ilaa 10000 nm gobolka oo leh hawlkarnimo 0.1 ilaa 10%)
    Shaandhooyinka dhuuban ee indhaha ee gobolka u dhow barta isotropic (0.4974 m at 300 °K), band gudbinta oo lagu hagaajinayo heerkulka kala duwan
    Kor-u-beddelka sawirka shucaaca laysarka ee CO2 una beddelo IR-u-dhow ama gobol muuqda iyadoo la isticmaalayo/ama la isticmaalayo Nd:YAG, ruby ​​ama leysarka dheeha leh waxtarka ilaa 30 %
    Guryaha aasaasiga ah
    Halbeegyada Lattice a = 5.757, c = 10.311 Å
    Iskuxidhka aan tooska ahayn ee 10.6 um d36 = 12.5 galabnimo/V
    Heerka waxyeelada indhaha oo ah 10.6 um, 150 ns 10 - 20 MW/cm2
    barbar socda dhidibka c 12.5 x 10-6 x °C-1
    toosan ilaa dhidibka c -13.2 x 10-6 x °C-1
    Dhismaha Crystal Tetragonal
    Qiyaasaha Unugyada a=5.756 Å, c=10.301 Å
    Meesha dhalaalaysa 997 °C
    Cufnaanta 4.702 g/cm3
    Mohs Hardness 3-3.5
    Iskuxidhka Nuugista 0.6 cm-1 @ 10.6 µm
    Joogtada Dielectric Qaraabo @ 25 MHz ε11s=10ε11t=14
    Iskuxidhka Balaadhinta kulaylka ||C: -13.2 x 10-6 /oC⊥C: +12.5 x 10-6 /oC
    Habdhaqanka kulaylka 1.5 W/M/°C

     

    Qiyaasta Farsamada
    Wavefront qalloocan in ka yar λ/6 @ 633 nm
    Dulqaadka cabbirka (W +/-0.1 mm) x (H +/-0.1 mm) x (L +0.2 mm/-0.1 mm)
    Bannaanka daloolka > 90% aagga dhexe
    Fiican λ/6 @ 633 nm ee T>=1.0mm
    Tayada dusha sare xoqo/qodo 20/10 kiiba MIL-O-13830A
    Isbarbar yaac ka fiican 1 arc min
    Si toos ah 5 daqiiqo oo arc ah
    Dulqaadka xagasha Δθ < +/-0.25o, Δφ < +/-0.25o

    测试图1图片2

    Qaabka

    Alaabta Cabbirka Hanuuninta Dusha sare Buurta

    Tirada

    DE0053

    AGS 5*5*0.5mm θ=41.3°;φ=0° AR/AR@1.1-2.6μm+2.6-12μm Dejinta

    1

    DE0093

    AGS 8*8*1mm θ=39°;φ=45° Labada dhinacba way dhalaaleen φ25.4mm

    3

    DE0119-0

    AGS 8*8*1mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm φ25.4mm

    3

    DE0119-3

    AGS 8*8*1mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm Dejinta

    2

    DE0119-1

    AGS 8*8*1mm θ=37°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm Dejinta

    3

    DE0149

    AGS 8*8*0.38mm θ=41.6°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm Dejinta

    1

    DE0367

    AGS 8*8*0.4mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm φ25.4mm

    1

    DE0367-0

    AGS 8*8*0.4mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm Dejinta

    1

    DE0367-1

    AGS 8*8*0.4mm θ=37°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm Dejinta

    3

    DE0367-2

    AGS 8*8*0.4mm θ=37°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm φ25.4mm

    1